Coffee Bag Vent

ABSTRACT

A laser formed vent in packaging material, formed by an interior breach and an exterior breach, which are connected to one another by a channel. The next interior breach an exterior breach are laterally offset from one another, the channel is formed by vaporizing a bubble in an interior layer, for example a foil layer. In one embodiment, the bubble can be crushed, but returns to its original configuration.

This application claims priority from Provisional application No. 62/331,352, filed May 3, 2016, the entire contents of which are herewith incorporated by reference.

BACKGROUND

Roasted coffee creates outflow of gas after its roasting. For example, 1 kg of fresh roasted coffee bean could generate about 10 liters of CO2 gas at a decreasing rate from the time of roasting. It can be important to package the coffee in a way that keeps its freshness while compensating for this gas generation.

A packaging film that is a high barrier to oxygen and moisture is typically used in packaging to preserve the coffee from degrading. An airtight flexible package would accumulate CO2 gas and build air pressure until the package ruptures. A common solution in use today is to install a 3 piece molded plastic valve that is welded to the interior of the coffee bag. The film material is mechanically breached within the circular valve weld to allow CO2 to escape though the valve and the breach in the film. The valve prevents air from entering the package but allows the CO2 to vent. A vent that allows CO2 to escape must also address the negative effects of allowing the fresh roasted aroma from escaping as well as allowing oxygen and moisture from entering the package which will degrade the sensory aspects of the coffee as well as shorten the shelf life. Other packaged items other than coffee also have an off gassing effect that would benefit from this type of vent, with or without a sealing film valve.

SUMMARY

The present invention creates a package from a packaging film, and uses a laser etching process to create a vent in the package film itself. This eliminates the expensive 3 piece molded valve. As such, this offers a better and more economical solution to eliminate CO2 gas buildup.

A laser etched or scored pattern on packaging film used in coffee bags is disclosed. This pattern can be used with or without an additional sealing film valve. This pattern provides a higher performance and lower cost packaging solution by releasing the buildup pressure caused by the emission of CO2 gas from fresh roasted coffee beans and grounds inside the coffee bag.

BRIEF DESCRIPTION OF THE DRAWINGS

In the Drawings:

FIG. 1 shows a drawing of common film construction for flexible packaging;

FIGS. 2A and 2B show an embodiment with a breach allowing gas escape;

FIG. 3 shows using the focused CO2 laser beam for processing;

FIG. 4 shows another embodiment with the CO2 laser beam processing a EVOH barrier;

FIG. 5 shows processing using a short wavelength laser;

FIG. 6 illustrates forming the interior breach with a laser;

FIGS. 7A and 7B show an embodiment using a short wavelength laser to process the material;

FIGS. 8A,8B and 8C show an embodiment using an exterior sealing film valve;

FIGS. 9A-9C show an alternative embodiment using concentric circles for sealing;

FIGS. 10A-10B show a delaminated area to prevent oil from blocking the airflow;

FIG. 11 illustrates the exterior of the package showing the exterior breach opening;

FIG. 12A-12B shows an embodiment using a laser etched vent and seal film valve; and

FIG. 13A-13B show an embodiment where the laser etched vent is formed on a patch.

DETAILED DESCRIPTION

Embodiments describe a laser etched vent that addresses many of the problems discussed above.

An embodiment is described herein may form the package using the techniques described in our patent application Ser. No. 13/899,387, filed May 21, 2013.

Advantages to the laser etched vent include, but not limited to:

Lower cost

No additional material or additional steps in the manufacturing process are required other than the packaging film itself or film type valve. These parts are much less expensive than the standard 3 piece molded valve and its complicated welding process to the package film.

Overall film thickness can be reduced considerably from the usual basic film construction of flexible packaging for retail coffee as shown in FIG. 1. Extra layers of polyester (PET) have been used as shown in the embodiment of FIG. 1, in order to strengthen the film structure so that the valve can be molded to the package. Embodiments as described herein do not require the valve to be welded and hence the package can be made thinner and less expensive.

Another advantage of this system is ease of production and process flow.

The laser etched vent with or without the additional sealing film valve can be created and applied onto any roll stock prior to packaging coffee. As described herein, the vent can be formed in a way that allows the vent to be crushed, in order to roll the packaging film onto the roll stock. Then, when the roll is unrolled, the laser etched vent will inflate in size. In contrast, the standard 3 piece valve must be welded onto the packaging film at the time of packaging the coffee. This requirement is because the roll stock of packaging film cannot be rewound after the bulky standard valve has been welded in place on the film.

Better oxygen and moisture barrier. The laser etched vent can be designed to vent exactly to the requirements for any type of coffee bean, ground or whole bean, which currently packaged in coffee bags.

The laser etched vent can be tailored to have the properties of a smaller aperture. This in turn will allow the specific amount of CO2 to escape and will in turn restrict air from outside of the package to enter. This will prevent excessive amounts of oxygen and moister to spoil the coffee. The addition of a sealing film valve further restricts outside air from entering thus extending the shelf life of the coffee within the bag.

Construction and design of laser etched vent utilizes the structure of a flexible packaging film.

A common film construction of flexible packaging for retail coffee is shown in FIG. 1.

An exterior printed polyester (PET) layer(s) 100, 102 forms the outer layer of the cross section of the package. The outer layer is underlied by an intermediate barrier layer 110. This intermediate layer 110 is typically formed of a foil metalized layer, e.g., a metalized PET, aluminum foil, or ethylene-vinyl-alcohol (EVOH) material. There can be an optional additional layer 115 of PET or PA (polyamide Nylon) on the interior surface of the barrier layer 110. The interior layer 120, that holds and packages the product is formed of polyethylene (PE) or polypropylene (PP) and often an additional sealing layer 125. Normally this can also be PE or PP.

The embodiments described herein explain formation of a laser etched vent. One embodiment forms the vent by using the selective absorption of different frequencies of laser light in each of multiple layers of a packaging film.

A breach is formed as shown in FIGS. 2A and 2B, allowing for CO₂ to escape. The breach 200 is defined by interconnected features formed into common high barrier coffee packaging film.

The film that is used can commonly range in thickness of 50 to 180 microns (0.002″ to 0.007″), although other thicknesses can be used. In this embodiment, the breach is formed through three layers, including an interior layer 215, an intermediate layer 220, and an outer layer 230. The interior layer 215 can be for example a PE,PE-PET, PP or PP-PET sealing layer. PET represents polyester. The sealing layer is commonly PE or PP with or without a PET or PA. Other materials are possible including co polymers The interior breach 210 is at a first lateral location in the interior layer 215. The interior breach then forms a channel 225 between an inner wall of the interior layer 215 and an outer wall of the intermediate layer 220. The intermediate layer 220 may be formed of different materials, and in this embodiment is formed of a metalized layer, foil, or EVOH. The interior breach 210 is formed at a first lateral location, which leads via the channel 225 to a second lateral location where is located the exterior breach 240. The channel is formed along the surface of the intermediate layer without compromising the exterior or interior layers. The channel also extends into the interior, as shown for example in FIG. 2B. The channel 225 causes the interior layer 215 to bulge at areas surrounding the channel. This forms an area which allows gas to extend through the channel from the interior breach to the exterior breach.

The exterior breach is formed in both the intermediate layer 220 and the exterior layer 230, where the exterior layer 230 can be formed, for example, of printed layers of PET.

The breaches are sized sufficiently to expel the CO2 gas evolved from the material inside, preferably coffee, without increasing the interior pressure of the package beyond an acceptable point. The design of the laser etched vent preferably does not exceed the maximum required air flow by more than a safety factor, as a determined percentage over the known rate to reduce the risk of excessive pressure buildup. The restriction to air flow is proportional to a factor of the intermediate breaches' cross sectional area and length. One embodiment may use multiple long narrow channels that would release the same amount of CO2 and have a lower OTR value.

Limiting the airflow though the etched feature to little more than the maximum required amount also limits the amount of oxygen and moisture that is allowed into the package. Oxygen and moisture being allowed into the package tends to degrade the coffee in the package. The gradual generation of CO2 flowing though the etched feature effectively eliminates the counter flow of exterior air and moisture from entering the package when the velocity of CO2 flowing out of the package is greater than the diffusion rate for Oxygen or water vapor. The flow of exterior air and moisture into the package is restricted to conditions where the interior pressure of the package is equal to or less than the exterior air pressure, that is to say after the CO2 gas has evolved from the coffee beans or grounds. The addition of another layer covering the exterior breach, e.g., a sealing film valve further limits the counter flow of air into the package while only restricting the exhaust of CO2 slightly.

According to another embodiment, the channels are sized as to seal or partially seal with the gradual swelling from absorption of oil from the coffee into the PE or PP interior layer. This swelling would decrease the ability to vent CO2 as the amount of CO2 that needed to be vented decreased. This sealing would decrease the ability of oxygen and moisture, however, from entering the package.

FIG. 11 illustrates the exterior of the package with the exterior breach opening 1100 in the packaging film 1110. A sealing film valve 1120 overlies the exterior breach, to even further limit the counter flow of air.

The counter flow of oxygen into a package, as measured by Oxygen Transmission Rate (OTR), per laser etched vent feature and without a sealing film valve is around 1.5 to 0.01 ml per day depending on the design of the vent, specifically the length and the cross sectional area of the channel. The design of the vent is dependent on the venting characteristics and amount of the roasted coffee. A wetted layer (sealing film valve 1120 wetted with oil, as described herein) covering the exterior breach reduces this amount to less than 0.01 ml per day. The industry standard molded valve weld is rated at 0.05 ml per day. A small perforation of 65 microns (0.0026″) in diameter directly though the packaging will exhaust CO2 at a rate over 100 times the maximum required rate (deflates 500 ml of CO2 at 1 PSI in 30 minutes) and has a very high OTR of 143 ml per day. While the channels and breeches in the 3 part laser etch vent are in the 50 to 200 micron range, their combined OTR and air release values are equivalent to a hole that is 0.7 microns (0.00003″) in diameter. At a channel cross sectional area and length that would be equivalent to a hole the diameter of 0.7 microns, each laser etched vent would allow an OTR transfer of around 1.5 ml per day and deflate 500 ml CO2 at 1 PSI in around 24 hours. Alone, the laser etched vent would be sufficient to preserve the coffee in the package to a period of time after the all CO2 has been exhausted. The addition of a sealing film vent would extend the preservation time well beyond the CO2 being exhausted and past coffee in a bag using the standard 3 piece molded valve.

Laser converting the packaging material lowers the cost by eliminating the 3 piece molded valve. Laser converting also increases the efficiency of the production process by allowing the conversion to happen offline from the packaging operation. Cumbersome in-line installation of the 3 piece molded valve is required due to the valve's bulk prohibiting rolling the film on a core. Laser etching the vent offline, even with the addition of a sealing film valve, will not prevent the film from being rolled on a core or operations in standard flow wrap/filling equipment.

The following provides a more detailed description of the laser etching film structure.

1. Channel

A variety of lasers can be used to etch the channels that control the flow of CO2 and air. The United States Patent Publication 2015/0102022 A1 illustrates this method. The selective absorption of a focused CO2 laser beam, coherent light at 10.6 micron nominal wavelength, will preferentially absorb into a PET material more than PE and will mostly reflect off a metalized or foil layer, leaving the foil intact.

FIG. 3 illustrates a focused CO2 laser beam 300 applied to the interior side 311 of a film 310. This is applied through one of the layers, where the laser 300 is preferably absorbed by the PET portion of the interior layer 325, after it passes through the PE or PP portion of the interior layer, 320. The interior side of the film 310 has a PET layer 325 a PP or PE layer 320 forming the interior layer along with the sealer, which is covered with a foil barrier 330. The foil barrier 330 is covered by an exterior PET layer. A channel 350 is created between the foil barrier 330 and the interior PE layer 320 by a laser operating to vaporize the interior PET layer 325 at its focused location. The rest of the structure, including the sealing layer 320, the foil barrier 330, and the exterior PET layer 340 remains intact. Note that channel or chamber 350 causes a bulge in its area, where that bulge is shown extending both into the interior and to the exterior. However, the bulge can extend into only one of interior or exterior in other embodiments.

A preferred method of doing this is by applying a focused CO2 laser beam from the interior 320 of the film to a foil 330 that is in contact with a PET film 325. The resulting channel is created by the vaporizing the PET film. This will also result in lessening of the reduction of flow which could otherwise be caused by physically crushing the channel. The material that was vaporized leaves a void (or channel) that remains even after the film has been crushed, and is then relaxed.

An alternative embodiment removes material through vaporization to form the channel, with or without the resulting bulge.

Another embodiment shown in FIG. 4 uses a focused CO2 laser beam along with a material formed by a polypropylene or polyethylene layer and sealer 400 as the inner portion, an EV OH barrier 410 and an exterior PET layer 420. The energy from the laser beam is preferentially absorbed into the EV OH layer 410 when fired through either PE layer 400 from the inside of the package, or PET layer 420 from the outside of the package. When processed from the outside of the package, the print or colorant in the film on the exterior of the package may absorb and interfere with the etch operation by the laser. Depending on the material and application, the creation of a channel in the EVOH film also may compromise the barrier property of the film unless a second barrier layer is added as in the sealing film valve which extend over the channel features. The FIGS. 11 and 12A embodiments includes this second barrier layer. This layer can also serve as a sealing film valve.

A shorter wavelength laser such as a fiber laser, operating around a 1.06 micron wavelength can be used as in FIG. 5. FIG. 5 illustrates how this shorter wavelength laser 500 can be used with a packaging film formed with an inner layer 511 of poly propylene or polyethylene and a sealer which can also include an interior PET or PA layer, an intermediate layer 510 formed of foil or metallized PET, and an exterior PET layer 520. The laser will preferentially absorb into the foil and metalized layers 510 without effecting the rest of the lamination. The absorption on the surface of the metal creates a heat affected zone 515 that will vaporize a small amount of the contacting plastic and create a bubble that is caused from the increased air pressure of the generated vapor which forms the channel 515. By pulsing the laser at different locations, a channel of interconnected bubbles can be created. A channel created by the laser is mostly created by deforming the structure of the film and not removing material as in other methods. The deformation can be partially reversed by physically crushing of the film resulting in an inconsistent flow from feature to feature.

2. Interior Breach

FIG. 6 illustrates how the Interior breach 600 though the PE and PET layer to the channel can be accomplished with a focused CO₂ laser beam. The breach can be accomplished though application of more laser energy produced by the CO₂ laser resonator. A foil barrier layer as shown in embodiments described above can be used to act as a backstop to the additional power and prevent the laser from transmitting though the PE layer and breach the barrier and exterior PET layers. This creates a bubble area that has both a wide bubble part 610, and the channel part 620 which is therefore connected to the breach 600

The interior breach size has little effect on the overall flow rate of the three part system formed by the interior breach, channel, and exterior breach. The breach should be small or can in certain embodiments include features, such as a filter or strainer, to prevent coffee grounds or particles from blocking the channel. Such a feature created by the laser in a similar manner as the channels. The feature is an area of delamination of the interior and barrier layers that CO₂ gas would have to pass through to enter the channel on the way out of the package. The delamination area or channel grid area would increase overall air flow restriction very little and would create a place for coffee particles to settle or be filtered out before entering the channel and possibly blocking air flow through them.

Exterior Breach

FIGS. 7A and 7B illustrate an embodiment. A short wavelength laser such as a fiber laser 700 operating around 1.06 micron wavelength creates laser fire 702 directed at the layers, transmitting through a PP/PE layer 710, compromising the foil layer 715, and an exterior PET layer 720. This kind of laser is well suited to breaching foil layers. The laser wavelength is preferably absorbed by the foil while being transparent to most plastics, including the plastic layers 710 and 720. The breach can be completed by using the excess heat and particles thrown from the vaporized metal of the foil 715 to penetrate the exterior PET layer(s) 720. Excess heat can also reflect back though the interior layers 710, a layer of PET against the barrier layer operates to contain the reflected heat and vaporized particles better than a single layer of PE, thereby preventing an unwanted breach of the interior layer at the site of the exterior breach. The layer 710 can be a thicker PE/PET layer relative to the exterior layer 720, and this thicker layer on the interior also operates to reduce the chance of this unwanted breach. The breach from the channel to the exterior can also be completed by applying a focused CO₂ laser beam onto the exterior of the film intersecting the foil breach created by a fiber laser. Mechanical methods such as a die or needle can alternatively be used to create a breach from the interior and exterior of the film to the channel. FIG. 7B shows a cross section across the line 7B-7B in FIG. 7A showing the interior layer 710, the foil layer 715 and exterior layer 720. In this embodiment, the interior and exterior layers can also be substituted by multiple stacked layers, e.g., a PE/PP layer and a barrier layer or multiple other layers of plastic materials.

Exterior Seal: Sealing Film Valve

Previous embodiments show how Channels created by the CO2 or fiber lasers create a raised surface or ridge on both the interior and exterior of the film. The ridge can be crushed but returns to near original shape when pressure is released. This is because, in most cases, the film has a good memory for the ridge, caused by, at least in part, metal particles from the vaporized foil embedding into the interior and exterior layers, and binding those layers into their expanded shapes. The film also has a memory for the ridges by being heated during the formation of the bubble and cooling in the inflated state. The film cooling in the inflated shape defines its new natural or relaxed shape. The exception is when a certain kind of short wave laser is used to create the channel. The shortwave laser may harden the aluminum and it therefore does not rebound from being crushed. In this embodiment shown in FIG. 8A-8C, The ridges on the exterior of the film are used to create a sealing feature, which can be used in addition to the breach and channel that will restrict or prevent the counter flow of air into the package. This sealing feature may be located between the inner breach and outer breach. In FIG. 8A, the exterior (outer) breach 800 is surrounded by Channels 810, 812 that form circles or rings that circumscribe the exterior breach to assist in creating a seal. The seal is formed between the crest of the circular ridges and an additional layer of film 820.

FIG. 8B shows a cross-section of the FIG. 8A embodiment along the line 8B-8B. In this embodiment, the material is processed as described above to form the bubbles, to form bumps in the shape of rings of material such as 810, 812. The topmost portion of each of these bumps, e.g. 815 presses against the sealing film 820 that overlies the materials of the bumps.

This is shown in further detail in FIG. 8C where each bump has its top portion 815 pressing against the sealing film 820. The seal is increased and propagated by the addition of a light layer of oil or other wetting liquid or material that is attracted to the layer, shown as 825. The oil 825 creates an air tight seal between the film of the sealing film valve and the ridges of the package film.

In operation, gas pressure, e.g., CO2, inside the package can cause pressure that will vent through the seal between the bumps 815 and the film layer 820. After the pressure is released, the seal is re-formed. The oil 825 also helps to re-form the seal after it has been broken, for example, by escaping CO2 gas. The surface energy of the oil 825 forms a wetting meniscus between the sealing film 820 and the ridge 815 wherever the two are in contact. The meniscus draws the film to the ridge like a zipper closing.

The seal can also be formed with a low durometer rubber or gel like or a viscoelastic gel like the solidified mineral oil common in gel candles.

The film of the sealing film valve should lay completely flat on the circle to be most effective. If there is a gap between the ridge of the circle and the film, then outside air could get in to the exterior breach. One way in which such a gap could be formed is by a wrinkle in the film. An alternative embodiment is shown in FIGS. 9A-9C. The concentric circles, or enclosed shapes, of ridges rise above the exterior surface of the film to a near uniform height as shown in FIGS. 9A-9C. FIG. 9A shows a top view of the exterior of the package, showing the exterior breach 900, as well as interior additional ridge features 910. The location 920 of the interior breach is also shown. In addition, there are a number of concentric sealing circles 930, 940, 950 that can seal between outside air and the exterior breach. These sealing circles seal along a tangent plane to the surface of the film, as explained herein, in a way that avoids problems caused by folds or wrinkles in the film.

A cross-section along the line 9B-9B is shown in FIG. 9A. This shows a slice of three concentric circles, 930, 940, 950. Each circle part has ridges, with The circle part 930 pressed against by ridges 935, the circle part 940 having ridges such as 945, and the circle part 950 having ridges such as 955. Each of these generally form a plane tangent to the surface of the film. The use of the tangent plane for sealing may reduce the chances of wrinkles or folds in the sealing film generated by a single protruding feature. Any such wrinkles or folds prevent a complete perimeter wetted seal between the ridge features and the sealing film valve. An incomplete perimeter wetted seal would allow air to enter the interior of the sealing feature and to the exterior breach.

FIG. 9C shows a close-up detail of the exterior breach 900, opening onto a section of the surface and on a channel ridge 960. Locations of the ridges may be as shown in the cross section of FIG. 9B, thereby sealing between the outside air and exterior breaches.

The interior package pressure required to break the meniscus seal decreases as the area of the circle the seal is formed on increases. The total force is a factor of pressure applied over an area. The seal on the smallest diameter circle determines the cracking pressure of the valve. In one embodiment, the escaping CO2 is allowed to exit the exterior breach at a point that is lower than the raised surface of the ridges and sealing film. A wet seal encompassing the entire exterior breach would increase the cracking pressure by the inverse of the area of the exterior breach. The exterior breach 900 is located, in part, on a ridge created by a channel, according to an embodiment. An exterior breach that is created by a line that extends from a channel ridge to a non-etched surface as in FIG. 9C, will allow escaping CO2 gas to fill the inside of the circular seal and prevent uncontrolled backpressure.

Likewise, a pattern of ridges 910 on the inside of the concentric sealing features allows escaping CO2 to distribute and pressurize the entire area inside of the sealing feature and helps to maintain a parallel surface for the sealing film to contact.

The cracking pressure of the valve can be set or designed to a level that would reduce the effect of changes in the barometric pressure which often fluctuates as much as 0.3 PSI per week. If the cracking pressure is set to zero, the package would experience a negative pressure or partial vacuum each time the barometric pressure increases. This negative pressure would increase the likelihood that exterior air and moisture would infiltrate the package. The inventor believes that a cracking pressure of 0.3 PSI may be optimal to nearly eliminate the possibility of a negative pressure in the package due to barometric pressure changes.

The film that forms the seal is formed of a material that does not swell when exposed to the oil that is used on the interface of the seal. The layer of oil should be applied thick enough to form a complete meniscus on at least one of the concentric circles. Any oil in excess of forming a meniscus does not contribute much to the lowering of the OTR value. Excess oil may also increase the chances of oil flowing into the exterior breach. The exterior breach and the channel will increase in air flow resistance with the introduction of oil on their interior surfaces and too much oil may completely block the flow of CO2 escaping.

FIGS. 10A-10B illustrate an embodiment that has a feature to prevent oil from blocking of inhibiting the intended flow of air. The feature may include a delaminated area 1000 that inflates if infiltrated with oil. The inflation caused by the oil infiltration opens the air path to the exterior breach 1010. The area also creates a reservoir for any oil that enters the exterior breach 1010 and prevents the oil from entering the channels and possibly mixing with the coffee. FIG. 10B illustrates a cross section along the line 10B-10B in FIG. 10A.

This can be as further shown in FIGS. 12A and 12B; where FIG. 12A shows the laser etched vent feature 1200, which is etched into the packaging film over which a sealing film valve assembly is attached by pressure sensitive adhesive. FIG. 12B shows a cross sectional view along the line 12B-12B in FIG. 12A, showing how the valve 1200 is attached by adhesive 1220 on to a stiffening cover 1230 over the packaging film. According to another embodiment, The sealing film valve may also incorporate a pigment that is sensitive to different concentrations of CO2 gas. The pigment is visible from the outside of the package and can be used as an indicator as to whether the CO2 gas was being emitted from the vent. This can allow a user to tell at a glance how fresh the coffee is. When CO2 is being emitted from the package, the coffee is typically very fresh, thus enabling the pigment to indicate coffee freshness.

This stiffening layer 1230 that holds the package film and the sealing film flat to one another.

Another embodiment recognizes that gas generation in modified atmosphere packaging, or “MAP” sometimes builds up air pressure and the result is a package that balloons up. Some packages, however, may preferably be formed of a material 1301 that is not suitable for laser etching of a channel vent as in the previous embodiments. E.g., Some clear PETs or PEs may not be laser etchable. According to an embodiment, shown in FIG. 13A-13B, a special “patch” added to a PSA label in order to carry out pressure relief while maintaining the cosmetic appearance. In this embodiment, a small multilayer patch 1300 is attached to either the package, or, as shown in the embodiment, or to or as a lidding film such as a PSA label. The patch 1300 has a structure similar to coffee bag film as in FIG. 1. A vent is etched into the patch though the package or lidding film as shown in FIG. 13B. The vent 1310 has an inner breach 1315, channel 1320 and outer breach 1325. The vent 1310 relieves the pressure in the package and have a low enough OTR not to effect the MAP gases in the package. The operation can be very simple, e.g., a postage stamp sized (¾ inch by ¾ inch) coffee film PSA label 1300 is attached to the bag or lidding film 1301 by a label applicator. The patch move on the conveyor system under the lasers (CO2 and short wave) and be etched the same as the coffee film as in previous embodiments. The bag or lidding film may be cut with the CO2 laser but this does not affect the channel formation. The bag or lidding film being cut will not affect the package's integrity as the PSA patch will hold it together. For MAP packaged produce, the sealing film valve would not be needed because of the shorter shelf life. A similar “Patch” application with the sealing film valve could be used for longer lived MAP products like dried fruits and nuts, if desired.

This will allow a MAP package to be made out of clear PET (or other specialty material that cannot be processed by lasers as done herein) to show its contents and not rupture or balloon up.

Other embodiments are contemplated. For example, while the above embodiments have described a specific material, other materials could be included. Certain plastics which are laser transmissive, for example, can be used in place of the PE or PET described herein. Also, while these techniques can be used to protect coffee in a package, they can also be used to protect other materials in such a package.

Those of skill would further appreciate that these features can be carried out using different materials and different techniques different words and different shapes.

Also, the inventor(s) intend that only those claims which use the words “means for” are intended to be interpreted under 35 USC 112, sixth paragraph. Moreover, no limitations from the specification are intended to be read into any claims, unless those limitations are expressly included in the claims.

Where a specific numerical value is mentioned herein, it should be considered that the value may be increased or decreased by 20%, while still staying within the teachings of the present application, unless some different range is specifically mentioned. Where a specified logical sense is used, the opposite logical sense is also intended to be encompassed.

The previous description of the disclosed exemplary embodiments is provided to enable any person skilled in the art to make or use the present invention. Various modifications to these exemplary embodiments will be readily apparent to those skilled in the art, and the generic principles defined herein may be applied to other embodiments without departing from the spirit or scope of the invention. Thus, the present invention is not intended to be limited to the embodiments shown herein but is to be accorded the widest scope consistent with the principles and novel features disclosed herein. 

1. A packaging film with an integrally formed vent, comprising: a first layer of interior material; a second layer, of metallized layer foil; and a third layer of exterior material, said second layer being between first and third layers, at least one of said first layer and said third layer being formed of a material which allows laser to pass without being affected by the laser, and where said material is transmissive to the laser, said first layer having an interior breach at a first location, said third layer having an exterior breach at a second location laterally offset from said first location, and said second layer having a channel formed therein, only in a specified location which extends from said interior breach to said exterior breach, said channel being an area where said metallized layer foil of said second layer is at least partly removed throughout a complete length of the channel, and where the channel is expanded relative to a size of said second layer at a location other than said specified location and where the channel is not expanded at locations other than said specified location.
 2. The packaging film as in claim 1, wherein said channel is formed in areas where vaporized metal from the foil is embedded in at least one of said first layer or said third layer to expand the at least one of the first layer or third layer to form the expanded portion, and where there are other areas of said second layer where said channel is not formed, and in said other areas the vaporized metal from the foil is not embedded in the at least one of said first layer or said third layer and the at least one of the first layer or third layer is not expanded.
 3. The packaging film as in claim 1, wherein said channel is crushable to an original size of said second layer by a crushing force, and returns to its original shape after said crushing force is removed.
 4. The packaging film as in claim 1, wherein said exterior material includes printing thereon.
 5. The packaging film as in claim 1, further comprising a sealing valve covering and sealing said exterior breach, said sealing valve having a structure that automatically vents pressure over a specified pressure amount, but prevents gas influx.
 6. The packaging film as in claim 5, wherein said sealing valve includes a bump completely surrounding the exterior breach, and a separate layer which attracts to the bump and seals to the bump, at areas completely surrounding the exterior breach, to seal the exterior breach.
 7. The packaging film as in claim 6, wherein said bump includes a meniscus of wetting material that attracts said separate layer.
 8. The packaging film as in claim 1, wherein said channel extends into and expands only a portion of both the first layer and the third layer, to cause expanded bump areas in both the first layer and the third layer across only a part of the package, and not across the entire package.
 9. The packaging film as in claim 1, wherein the first layer of interior material forms a continuous interior surface of the package, the third layer of exterior material forms a continuous external surface of the package, the interior breach is formed in the first layer facing toward an inside of the package, the exterior breach is formed in the continuous exterior material facing away from a direction in which the interior breach is facing, and where the channel extends between the interior breach and the exterior breach and does not extend all the way across the package.
 10. A method of forming packaging film with an integrally formed vent, comprising: producing a laser output at a first location through a first layer of plastic material, to a second layer, of metallized layer foil, which is overlaid by a third layer of plastic material, creating a second breach in the third layer at a second location laterally offset from said first location; said producing creating a breach in the first location and creating a channel in the second layer, only in a specified location which extends from said first breach to said second breach, said channel defining an area which is expanded relative to a size of said second layer at other than said specified location, and forms a bump in said specified location, to create a channel as an expanded area between said first breach and said second breach.
 11. The method as in claim 10, wherein said producing creates said channel in areas where vaporized metal from the foil has become embedded in at least one of said first layer or said third layer.
 12. The method as in claim 10, further comprising crushing said channel to an original size of said second layer using a crushing force; and Removing said crushing force, whereby said channel returns to its original shape after said crushing force is removed.
 13. The method as in claim 10, further comprising a forming sealing valve sealing said second breach, said sealing valve allowing pressure over a specified pressure amount to vent, but preventing gas influx.
 14. The method as in claim 10, wherein said channel extends into and expands both the first layer and the third layer.
 15. A packaging film, comprising: a first layer of interior material of a plastic that allows laser to pass; a second layer including a metallized layer foil; and a third layer of exterior material of a plastic that allows laser to pass, said second layer being between first and third layers, said first layer having an interior breach at a first location, said third layer having an exterior breach at a second location laterally offset from said first location, and said second layer having a channel formed therein, only in a specified location which extends from said interior breach to said exterior breach and which does not extend all the way across said second layer and in the location of the channel where a material of said second layer is at least partly removed and outside of which location of the channel where the second layer is not removed and is intact, said channel being an area which is expanded to form a bump in said first layer and also to form a bump in said third layer in said specified location, to expand a distance between said first and third layers in said specified location, said bump formed with embedded parts of said second layer that are embedded into both said first layer and said third layer, and where said first layer in locations other than said specified location not having said embedded parts of said second layer therein.
 16. The packaging film as in claim 15, wherein said channel is crushable to an original size of said second layer, and returns to its original shape after a force is removed.
 17. The packaging film as in claim 15, further comprising another layer overlying said third layer, said another layer forming a sealing valve sealing said exterior breach against gas influx, but allowing pressure release from an interior of the film.
 18. The packaging film as in claim 17, wherein said sealing valve surrounds the exterior breach.
 19. The packaging film as in claim 15, further comprising a pigment in one of said layers, said pigment visible from an outside of said package, and changing color to indicate whether CO₂ is in contact with the pigment.
 20. The packaging film as in claim 15, wherein the packaging film is a pressure sensitive adhesive layer attached to a packaging material. 